i got some new development!!!!
well i didnt get to testing the dangerden scraps... BUT i did let the test that i already had going just do their thing... and here is what happened:
The redline is still doing just fine, and the coating process of the aluminum has not increased.... it pretty much stopped after a few days just as the purple ice did.
The purple ice was doing quite well untill recently. there is now a whiteish haze sittin on the bottom of the cup, and ontop of the metals... along with a slight coating to the cup. the half concentration has more of it than the full concentration.
the distilled water is doing just as well as the RedLine.
and the cup of tap water i added to the test (about 4 days into the test) has been coroding ALOT.
sooooo.... i THINK i have an answer to the redline vs purple ice question... but now what about the redline half and full strength.... guess we will have to wait and see.
it is pretty amazing that the distilled has not showed any signs of corrosion yet!!! i would imagine that in a computer, the heat would increase the chance of bacteria growing, which would add to the electrolicity (is that a word) of the water. So, i would still recommend redline over just distilled.
i will be taking pictures, but maybe a little later since i want to give some time for this stuff to build up so you can see it.
|