Fixittt
in part my error for not adding the 'standard' comment about the necessity for ALWAYS using a corrosion inhibitor when aluminum is in the system
(I have several Commercial wb reviews to be posted and saying always the same thing, I neglected to add such in the initial post here)
yes, your hoses are pink - so yes, it is doubtful you will see any corrosion
BUT
if you read around you will encounter no shortage of tales of WCing newcomers who did not
AND
if no corrosion inhibitor is used you WILL see corrosion
should I choose to do so, I can post many images of anodized parts showing corrosion, some after only days exposure to tap water
but what is the point ?
with corrosion inhibitor the material is serviceable
a good wb is a good wb, and should provide years of service
you will not find me saying that 'aluminum is as good as copper' because it is not
wtf does a hammer have to do with anything ?
YOU do not understand about what the brass barb comment was in reference to
go to OCAU, read up on the Silverprop corrosion spectaculars, eat your mis-informed words
MDE
you will see no hard data for such because it is contrary to fact
|